JAIC 1994, Volume 33, Number 3, Article 2 (pp. 247 to 255)
JAIC online
Journal of the American Institute for Conservation
JAIC 1994, Volume 33, Number 3, Article 2 (pp. 247 to 255)




All of the specimens examined showed that the earlywood appeared to be substantially intact, while the latewood showed severe cell distortion and damage, indicating significant deterioration. Figure 2, a micrograph of an untreated, matched control specimen taken at the boundary between two growth rings, shows latewood tracheids below and earlywood tracheids from the following year's growth above. The earlywood tracheids can be seen to be virtually indistinguishable from undeteriorated wood, and the spiral thickenings typical of Douglas fir are clearly visible on the lumen surface. It is not known why there should be such a difference in susceptibility to bacterial degradation between earlywood and latewood, but the nature of bacterial attack is generally not as well understood as other forms of biological deterioration. Supplementary examination by light microscopy using polarized light confirmed that the wood was bacterially degraded, as had been previously mentioned (Wang and Schniewind 1985), but there was also evidence of soft rot damage and in some specimens hyphae of decay fungi (brown rot) were found.

Fig. 2. Scanning electron micrograph of a cross section of deteriorated, untreated Douglas fir showing nearly destroyed latewood below and apparently intact earlywood above. Note the spiral thickenings inside the earlywood tracheids. 175�

The most striking finding of the SEM examination of specimens treated with consolidant was that many tracheids contained little if any resin, while others showed either solid plugs or thick inner sleeves of consolidant (fig. 3). Note that in the empty tracheids the spiral thickenings are clearly visible, while no such markings are shown on the inner surfaces of the resin sleeves. Some plugs had smooth, concave surfaces, suggesting that there were bubbles in the resin. Since most of the samples had been treated with a 20 wt% solution of resin, and since there had been evidence that complete saturation with consolidant solution had been achieved during vacuum impregnation (Wang and Schniewind 1985), it would have been expected that on average about 12–14% of the void space in the wood be filled with consolidant. (These values are less than 20% because the resins have higher density than the solvents.) That most tracheids were empty shows that considerable bulk flow of solution must have taken place during drying, resulting not so much in a uniform flow toward the specimen surfaces but rather a migration toward and deposition in certain tracheids. These tracheids could then serve as loci for further resin deposition and solvent vapor diffusion.

Fig. 3. Scanning electron micrograph of earlywood tracheids treated with 20 wt% B72 in toluene. Note the solid plug in the tracheid at the lower left and the thick sleeves of resin toward the top. Spiral thickenings clearly visible in other tracheids indicate little or no resin content. 265�

There did not appear to be any qualitative differences in the observed pattern of resin distribution that could be attributed to either type of resin or type of solvent, or even concentration of consolidant solution. However, it was noted that in Acryloid B72 the plugs or sleeves of consolidant almost always failed in the same fracture plane as the wood, while in Butvar B90 or B98 tubes of consolidant, identifiable by the spiral thickenings molded on their outer surfaces, could sometimes be seen protruding from the fracture plane. An extreme example of such protrusions is shown in figure 4. These protrusions may be due to higher tensile strength of the polyvinyl butyral, which would allow the sleeves or plugs to be broken at a weak point distant from the overall fracture plane. Since Butvar B98 has been shown to have adhesive qualities comparable to Acryloid B72 in acetone and much superior to B72 in toluene (Sakuno and Schniewind 1990), lack of adhesion of the Butvar resins is not a likely explanation for this phenomenon.

Fig. 4. Scanning electron micrograph of fracture surface of specimen treated with B98 in ethanol 3.5 mm from the end and close to the edge, showing sleeves and plugs protruding beyond the fracture plane. 175�

The tracheids containing plugs or sleeves of resin appear to be scattered irregularly throughout the wood structure, and visual examination of cross sections did not reveal any obvious distribution patterns. Plots were made showing the percentage of plugs and sleeves in sample areas near the surface and at the core as a function of distance from the end. Average plots for Acryloid B72 and Butvar B98, each for two different solvents, are shown in figures 5–8. It must be emphasized that the percentages given refer to the relative number of tracheids containing significant amounts of resin and are not measures of actual resin content.

Fig. 5. Percentage of tracheids with visible resin in specimens treated with 20 wt% B72 in acetone vs. location.

Fig. 6. Percentage of tracheids with visible resin in specimens treated with 20 wt% B72 in toluene vs. location.

Fig. 7. Percentage of tracheids with visible resin in specimens treated with 20 wt% B98 in ethanol vs. location.

Fig. 8. Percentage of tracheids with visible resin in specimens treated with 20 wt% B98 in ethanol-toluene vs. location.

The general trend seen in figures 5–8 is for more tracheids near the edge of the cross section to have significant amounts of resin than tracheids in the core, and also an increase in the percentage of tracheids with resin going from midlength of the specimen toward the end surface. The longitudinal variation is more clearly evident in the core positions than at the edge. In the case of B72 and either of its solvents, the shape of the longitudinal distribution follows a similar pattern for both core and edge. With B98 and either of its solvents, however, the percentage of tracheids with resin at the longitudinal position closest to the end is higher in the core than at the edge. This finding can be attributed to the much greater ease with which fluids move longitudinally through wood (Siau 1989), so that in this section the longitudinal movement predominates over lateral migration. B72 solutions have lower viscosity, which may change the balance of movement in this case. The plots shown in figures 5–8 are averages of four specimens each. Plots for individual specimens vary widely, many not showing clear trends.

Average values of the data that form the basis for figures 5–8 (i.e., the data for B72 and B98 excluding B90 and the one specimen treated with a 5 wt% solution of B98) are shown in table 1. Averaged over all treatments and positions, 15.9% of the earlywood tracheids contained visible consolidant. Average loading (i.e., gravimetrically determined resin content) was 29.4% for B72 in acetone, 32.2% for B72 in toluene, 28.2% for B98 in ethanol, and 31.8% for B98 in ethanol-toluene mixture. (Resin loading is a function not only of solution concentration but also of the porosity of the material being treated, so that solution concentration alone is not indicative of the resin loading that can be achieved.) The loading was therefore substantially the same for both resin types, but specimens treated with B72 had much lower percentages of earlywood tracheids containing visible resin as compared to those treated with B98. Solutions of B72 probably tend to migrate to selected tracheids more effectively owing to their much lower viscosity as compared to solutions of B98. The concept of more resin in fewer tracheids in the case of B72 is supported by the observation that the ratio of plugs to sleeves was much greater for B72—1.01 and 0.72 in acetone and toluene, respectively—as compared to B98—0.17 and 0.07 in ethanol and ethanol-toluene, respectively. The type of solvent appeared to have less of an effect.


For longitudinal position, table 1 shows that the location closest to the end of the specimens had by far the greatest percentage, 28.6%, of tracheids with consolidant. All of the interior positions had much smaller percentages, ranging from 10.6% to 16.1% but not in steadily decreasing order from the end to the most interior position. Lateral position within a given cross section indicates a substantially greater percentage of tracheids with visible resin near the cross section edge as compared to the core.

The data were subjected to an analysis of variance and associated statistical tests. The results of the basic three-way analysis of variance are shown in table 2. All of the main effects—treatment (resin-solvent combination), longitudinal position, and lateral position—were found to be statistically significant at better than the 1% level. Tukey multiple range tests showed that effect of treatment was due to resin type alone, solvent type showing no statistically significant effect. However, while B72 in toluene was significantly different from B98 in either of its solvents, B72 in acetone differed significantly only from B98 in the ethanol-toluene mixture. The significance of longitudinal position was entirely due to the high percentage of tracheids with resin at the end position. All other longitudinal positions were not significantly different from each other. All the findings are reflected in the 95% confidence limits in table 1. Where the intervals overlap, the differences are not statistically significant, whereas significant effects are characterized by intervals that do not overlap.


No statistical analyses were made for the specimens treated with B90, but the results for the few specimens examined were similar to those for specimens treated with B98. The one specimen treated with 5 wt% B98 in ethanol-toluene also showed a similar pattern of migration, but since the loading was only 7.5%, there were far fewer tracheids with visible resin.

The results have shown that there is consolidant migration during solvent evaporation by bulk flow from the interior toward specimen surfaces. Since there had been conclusive evidence of complete saturation of the material with consolidant solution, incomplete penetration during treatment is clearly ruled out as a factor. There is also internal migration to selected tracheids, so that in earlywood the consolidant appears to be concentrated on average in only 16% of the total number of tracheids. Since in the case of B72 the polar acetone that is adsorbed by wood and causes substantial swelling gives nearly the same results as non-polar toluene that does not swell wood, the diffusion of solvent vapor appears to take place through the porous structure rather than by diffusion through the cell walls in the form of solvent vapor bound to internal sorption sites. One can only speculate as to why the consolidants become concentrated in selected tracheids. One possible explanation might be that the resins form chemical complexes with tannins or decomposition products within the wood that initiate precipitation of resin in particular locations. It is not clear whether plugs and sleeves extend over the entire length of tracheids. In some cases plugs could be seen in association with bubbles, so that plugs and sleeves may alternate in the same tracheid. Some protruding sleeves and plugs were quite long, up to 1.3 mm, suggesting that if resin is present it extends over the entire length of the tracheid.

Completely uniform consolidation treatments may not be possible, either because complete penetration by consolidant solution cannot be achieved or because of a certain amount of reverse migration, as observed in the present study. In either case there will be more consolidant near the surface than in the interior, and this type of nonuniform distribution can be quite desirable in some instances. A greater concentration of consolidant in the surface layers will, for instance, improve surface hardness and abrasion resistance and will also result in greater improvement of bending strength as compared to a uniform distribution. The latter comes about because the surface layers contribute disproportionately to the resistance against flexural loads. Some degree of reverse migration can therefore be beneficial and a valuable attribute of the treatment in particular circumstances.


Appreciation and thanks are due Julie Trosper, who assisted with this project as a volunteer. Discussions with S. L. Quarles and T. G. Rials of W. W. Wilcox were very helpful and are gratefully acknowledged.